Functional Polymer - Compatibilizing Masterbatch
We supply functional polymers including coupling agents, compatibilizers, impact modifiers and adhesive resins.
We offer a wide variety of products for applications, including automotive, multi-layer film, industrial and packaging.
We offer world-class technology and global availability. Our products can be used with polyolefins and engineering resins.
Soltex
COUPLING AGENTS & IMPACT MODIFIERS
PP - Coupling Agents
| Grade | Melting Point °C | MFI 190° / 2.16 Kgs | Maleic Anhydride Content in % | Applications |
|---|---|---|---|---|
|
5505 |
165 |
105 |
1.5 |
PP / Glass |
|
5515 |
165 |
195 |
1.4 |
PP / Long Glass |
|
5525 |
160 |
145 |
1.8 |
Wood & Natural Fillers |
|
5535 |
155 |
100 |
1.2 |
PP / Glass Heat Stability |
|
5545 |
155 |
110 |
0.9 |
PP / Glass Low Emission |
|
5820 |
165 |
105 |
1.7 |
PP / Glass Micro Pellets |
|
5790 |
145 |
150 |
1.0 |
PP / Glass Low Emission |
|
5980 |
170 |
>395 |
>1.5 |
PP / Glass & WPC |
|
5840 |
135 |
>395 |
>1.5 |
PP / Glass sizing |
PE - Coupling Agents
| Grade | Base Polymer | MFI 190° / 2.16 Kgs | Density gram / cm3 | Maleic Content in % | Applications |
|---|---|---|---|---|---|
|
9140 M |
Metallocene HDPE |
3.5 |
0.975 |
1.4 |
Wire & Cables compounds |
|
9160 M |
Metallocene HDPE |
1.8 |
0.975 |
>1.5 |
WPC Compounds |
|
9265 M |
Metallocene MDPE |
1.5 |
0.945 |
>1.5 |
WPC & Recycle Compounds |
|
9170 M |
Metallocene LLDPE |
1.4 |
0.910 |
1.2 |
Wires & Cables |
|
9470 |
LLDPE |
0.9 |
0.920 |
1.0 |
Wires & Cables |
|
9570 M |
Metallocene LLDPE |
3.8 |
0.918 |
1.6 |
WPC & Recycle Compounds |
Impact Modifiers for Nylon Compounds
| Grade | Base Polymer | Melting Point C° | Density gram / cm3 | Applications |
|---|---|---|---|---|
|
3050 NL |
EPDM |
65 |
0.85 |
Ultra high viscosity for high melt strengths |
|
3060 NL |
Ethyl a Olefin |
55 |
0.89 |
High viscosity |
|
3065 NL |
Ethyl a Olefin |
60 |
0.89 |
High Flow |
|
3070 NL |
Ethyl a Olefin |
50 |
0.85 |
High flow – low temp impact resistance |
|
3075 NL |
Ethyl a Olefin |
120 |
0.9 |
Medium performance economy grade |
|
3080 NL |
Ethylene Octane |
60 |
0.85 |
Octane base |
Compatilizers for Recycle Compounds
| Grade | Base Polymer & Applications | Performance |
|---|---|---|
|
2700 R |
ABS, PC / ABS |
Improves compatibility and mechanical properties |
|
2720 R |
PP / Nylon post consuming carpets |
Improves compatibility and mechanical properties |
|
2730 R |
Wood plastics composites PE base |
Improves mechanical properties, reduces water up-tacking |
|
2740 R |
Wood plastics composites PP base |
Improves mechanical properties, reduces water up-tacking |
|
2750 R |
Post consuming PE / PP / PA / EVOH mix |
Improves compatibility and mechanical properties – Reduces deviation |
ADHESIVE TIE LAYER RESINS
EVA BASED TIE RESINS
| Grade | Melting Point °C | MFI 190° / 2.16 Kgs (g / 10 min) | Density gram / cm3 | Vicat Softening Point °C / °F |
|---|---|---|---|---|
|
6380 EV |
87 /188 |
0.8 |
0.89 |
60 / 140 |
|
6385 EV |
82 / 179 |
1.5 |
0.97 |
65 / 149 |
TIE RESINS FOR ALUMINIUM COMPOSITE PANELS
| Grade | MFI 190°/ 2.16 Kgs (g / 10 min) | Base Polymer | Density gram / cm3 | Melting Point °C / °F | Vicat Softening Point °C / °F |
|---|---|---|---|---|---|
|
6670 AL |
1.4 |
PE |
0.950 |
125 / 257 |
88 / 190 |
|
6680 AL |
1.7 |
EVA |
0.925 |
90 / 194 |
67 / 152 |
MODIFIED POLYOLEFIN
| Grade | MFI 190° / 2.16 Kgs (g / 10 min) | Melting Point °C / °F | Density gram / cm3 | Vicat Softening Point °C / °F |
|---|---|---|---|---|
|
PMOD 700 |
1.8 |
120 / 248 |
0.95 |
85 / 185 |
|
PMOD 710 |
2.4 |
45 / 113 |
0.80 |
- |
POLYSTYRENE BASED TIE RESINS
| Grade | MFI 190° / 2.16 Kgs (g / 10 min) | Melting Point °C / °F | Density gram / cm3 | Vicat Softening Point °C / °F |
|---|---|---|---|---|
|
8875 PS |
1.57 |
127 / 260 |
0.96 |
90 / 194 |
|
8895 PS |
1.45 |
124 / 255 |
0.94 |
84 / 183 |
|
8805 PS |
1.72 |
126 / 258 |
0.93 |
83 / 181 |
PET BASED TIE RESINS
| Grade | MFI 190° / 2.16 Kgs (g / 10 min) | Melting Point °C / °F | Density gram / cm3 | Vicat Softening Point °C / °F |
|---|---|---|---|---|
|
PETR 1050 |
2.6 |
110 / 230 |
0.10 |
54 / 129 |
|
PETR 1060 |
1.9 |
84 / 183 |
0.95 |
- |
|
PETR 1075 |
1.7 |
111 / 231 |
0.85 |
80 / 176 |
PP BASED RESIN FOR BOPP APPLICATIONS
| Grade | MFI 190° / 2.16 Kgs (g / 10 min) | Melting Point °C / °F | Density gram / cm3 | Vicat Softening Point °C / °F |
|---|---|---|---|---|
|
BP 7000 |
4.8 |
148 / 298 |
0.95 |
107 / 224 |
ADHESIVE TIE LAYER RESINS
PP BASED TIE RESINS
| Grade | Melting Point °C / °F | MFI 190° / 2.16 Kgs(g / 10 min) | Density gram / cm3 | Vicat Softening Point °C /°F |
|---|---|---|---|---|
|
5550 rPP |
155 / 311 |
4.3 |
0.10 |
128 / 262 |
|
5560 rPP |
145 / 293 |
4.6 |
0.91 |
115 / 239 |
|
5580 CoPP/rPP |
158 / 316 |
2.8 |
0.93 |
143 / 289 |
|
5595 CoPP |
150 / 302 |
22 |
0.89 |
88 / 190 |
PE BASED TIE RESINS FOR BI-ORIENTED FILM
| Grade | MFI 190° / 2.16 Kgs(g / 10 min) | Melting Point °C /°F | Shore Hardness D - scale | Density gram / cm3 | Vicat Softening Point °C /°F |
|---|---|---|---|---|---|
|
9920 B |
3.9 |
118 / 244 |
41 |
0.87 |
84 / 183 |
|
9930 B |
2.5 |
97 / 206 |
33 |
0.85 |
65 / 149 |
READY TO USE PE BASED TIE RESINS
| Grade | MFI 190° / 2.16 Kgs(g / 10 min) | Melting Point °C /°F | Density gram / cm3 | Vicat Softening Point °C /°F |
|---|---|---|---|---|
|
9050 m LLDPE |
5 |
122 / 251 |
0.925 |
95 / 203 |
|
9060 m LLDPE |
1.9 |
125 / 257 |
0.94 |
102 / 215 |
CONCENTRATED PE BASED TIE RESINS
| Grade | MFI 190° / 2.16 Kgs(g / 10 min).1Kgs(g / 10 min) | Melting Point °C /°F | Density gram / cm3 | Shore Hardness D -scale | Vicat Softening Point °C /°F |
|---|---|---|---|---|---|
|
9965 |
3.9 |
118 / 244 |
0.925 |
50 |
100 / 212 |
|
9975 |
1.7 |
115 / 239 |
0.930 |
45 |
102 / 215 |
|
9985 |
1.4 |
120 / 248 |
120 / 248 |
35 |
80 / 176 |
|
9995 |
0.9 |
125 / 257 |
0.910 |
55 |
115 / 239 |